Component A Topsealer WT Dragon Gloss 3L

Two-component water-based polyurethane varnish with a glossy finish. Designed to protect microcement surfaces, it offers high resistance to wear, chemical agents, and scratching without yellowing. Compatible with multiple substrates such as wood, parquet, stamped concrete, or microcement, its formulation with hydroxylated polyester resins and isocyanates allows it to maintain vapor breathability and ensures durability both indoors and outdoors.

Component A must be mixed with Component B in a 3:1 ratio (by weight) by gently stirring and allowed to rest for 30 minutes before application. Its pot life is 60 minutes at 20 °C. It is applied in two coats (14–24 h between them), with a total coverage of 5‑8 m²/L (two coats), and dries completely after 7 days, achieving a Persoz hardness of 250 s. Ideal for high-traffic areas, humid areas, and embellishing industrial surfaces with a deep glossy finish.

Main Features

1. Intense Gloss: Glossy finish that enhances the color and texture of the substrate.
2. High Chemical and Mechanical Resistance: Protects against water, alkalis, bleach, oil, vinegar, wine, and alcohol without visible marks.
3. Non-yellowing: Maintains transparency even outdoors with sun exposure.
4. Compatible and Breathable: Applicable on microcement, wood, concrete, and parquet, respecting vapor breathability.
5. Easy Professional Application: Can be applied with a brush, roller, or spray gun; quick and easy mixing, ideal for indoor and outdoor projects.

Instructions for Use

1. Shake Component A and let it rest for 30 minutes.
2. Mix with Component B in a 3:1 ratio (by weight), stirring at low speed.
3. Apply two coats, allowing 14‑24 hours drying time between them.
4. Observe application temperature between 15 °C and 30 °C.
5. Full cure in 7 days to achieve complete resistance.

Coverage

• 5–8 m²/L in total for two correctly applied coats.

Technical Specifications

• Nature Comp. A: Water-based polyacrylate
• Density: 1.03 ± 0.01 g/cm³
• Viscosity (23 °C): 130–150 mPa·s
• Solids Comp. A: 22–23 %
• pH Comp. A: 7–8
• Pot life: 60 min at 20 °C
• Persoz Hardness (7 days): 250 s
• VOC (A+B): < 5 g/L
• 
  

Storage Conditions

Store in a cool, dry place, protected from direct sunlight, between 10 °C and 30 °C. Keep in its original closed container. Shelf life of 12 months from manufacturing.